Suprasil 3001 Material Grades For The Infrared Spectrum
Description
Suprasil® 3001, 3002 and 300 are high purity synthetic fused silica materials manufactured by flame hydrolysis. They combine excellent physical properties with outstanding optical characteristics from the UV to the near IR. During the manufacturing process an intermediate drying step reduces the OH content of the Suprasil® 300x to below 1 ppm. A chlorine content of 1000 ppm – 3000 ppm is material inherent and results in a slight shift of the UV-absorption edge to the longer wavelength region. The Suprasil® 300x family of materials has the combination of ultra low total metal impurities (< 1 ppm) and low OH (< 1 ppm) that result in no absorption bands from the visible to the IR spectral region. This property makes this material family the ideal choice for any low absorption application in the near-IR.
Suprasil 3001 Material Grades For The Infrared Spectrum
Specifications |
|
|---|---|
| Application Spectrum: | Deep Ultraviolet (DUV), Ultraviolet (UV), Visible (VIS), Infrared (IR), Near Infrared (NIR), Broadband |
| Wavelength Range: | 200-3500 nm |
For pricing, technical or any other questions please contact the supplier
- No registration required
- No markups, no fees
- Direct contact with supplier
Contact Supplier
How to order?
-
Ships from:
Germany
-
Sold by:
-
On FindLight:
External Vendor
Claim Heraeus Page to edit and add data
Frequently Asked Questions
Infrasil® 301 and 302 are optical quartz glass grades manufactured by fusion of natural quartz crystals in an electrically heated furnace.
Suprasil® 3001, 3002 and 300 are high purity synthetic fused silica materials manufactured by flame hydrolysis.
A chlorine content of 1000 ppm – 3000 ppm is material inherent and results in a slight shift of the UV-absorption edge to the longer wavelength region.
The Suprasil® 300x family of materials has the combination of ultra low total metal impurities (< 1 ppm) and low OH (< 1 ppm) that result in no absorption bands from the visible to the IR spectral region. This property makes this material family the ideal choice for any low absorption application in the near-IR.
An intermediate drying step reduces the OH content of the Suprasil® 300x to below 1 ppm.